C3216X8R1H154K TDK Corporation, C3216X8R1H154K Datasheet - Page 10

• Manufacturer Part Number: C3216X8R1H154K
• Description: CAP CER .15UF 50V X8R 10% 1206
• Manufacturer: TDK Corporation
• Series: Cr

Specifications of C3216X8R1H154K

• Capacitance: 0.15µF
• Tolerance: ±10%
• Package / Case: 1206 (3216 Metric)
• Voltage - Rated: 50V
• Temperature Coefficient: X8R
• Mounting Type: Surface Mount, MLCC
• Operating Temperature: -55°C ~ 150°C
• Features: High Temperature
• Applications: General Purpose
• Size / Dimension: 0.126" L x 0.063" W (3.20mm x 1.60mm)
• Thickness: 0.85mm
• Voltage Rating: 50 Volts
• Temperature Coefficient / Code: X8R
• Product: General Type MLCCs
• Termination Style: SMD/SMT
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Ratings: -
• Lead Spacing: -
• Lead Free Status / Rohs Status: Lead free / RoHS Compliant
• Other names: 445-3434-2; C3216X8R1H154KT

• All specifications are subject to change without notice. Please read the precautions before using the product.
US Catalog // C Series — High Temperature Application // Version A11
No.
9
10
11
General
Specifications
Item
Solderability
Resistance to solder heat
External
appearance
Capacitance
D.F. (Class 2)
Insulation
Resistance
Voltage
Proof
Vibration
External
appearance
Capacitance
D.F. (Class 2)
Performance
New solder to cover over 75% of
termination.
25% may have pinholes or rough spots
but not concentrated in one spot.
Ceramic surface of ”A sections” shall
not be exposed due to melting or
shifting of termination material.
No cracks are allowed and terminations
shall be covered at
least 60% with new solder.
Meet the initial spec.
Meet the initial spec.
No insulation breakdown or
other damage.
No mechanical damage.
Meet the initial spec.
Characteristics
Class 2
Characteristics
Class 2
C Series — High Temperature Application
X8R
X8R
A section
Change from the
value before test
± 7.5 %
Change from the
value before test
± 7.5 %
Test or Inspection Method
Completely soak both terminations in
solder at 235±5ºC for 2±0.5s.
Solder: H63A (JIS Z 3282)
Flux: Isopropyl alcohol (JIS K 8839)
Completely soak both terminations in solder at
260±5ºC for 5±1s.
Preheating condition
Flux: Isopropyl alcohol (JIS K 8839)
Solder: H63A(JIS Z 3282)
Leave the capacitor in ambient conditions for 48±4h
before measurement.
Reflow solder the capacitor on a P.C. board (shown in
Appendix 1) before testing.
Vibrate the capacitor with amplitude of 1.5mm P-P
sweeping the frequencies from 10Hz to 55Hz and back
to 10Hz in after 1min.
Repeat this for 2h each in 3 perpendicular directions.
Temp. : 150±10ºC
Time : 1～2min.
Rosin (JIS K 5902) 25% solid solution.
Rosin (JIS K 5902) 25% solid solution.