DP-100-CLEAR 3M, DP-100-CLEAR Datasheet - Page 3

• Manufacturer Part Number: DP-100-CLEAR
• Description: Adhesive; Epoxy; Clear
• Manufacturer: 3M

Specifications of DP-100-CLEAR

• Chemical Component: Epoxy Resin
• Chemical System: Epoxy
• Color: Clear
• Dispensing Method: Syringe
• Primary Type: Adhesive
• Time, Drying: Air Dry for 15 minutes, Force Dry for 10 minutes @ 66 °C +⁄- 5 °C (Aluminum Surface), If 3M™ Scotch-Weld™ Structural Primer 1945 B⁄A is Used, Apply a Thin Coating (0.5 mils) on the Metal Surfaces to be Bonded, Air Dry for 10 minutes, then Cure for 30 minu
• Time, Setting: 15 min. (Aluminum), 10 min. (Steel)
• Weight: 1.7 Oz.
• Lead Free Status / Rohs Status: RoHS Compliant part

Scotch-Weld
Epoxy Adhesives
DP-100 Clear • DP-100 NS Translucent
Typical Cured
Properties
TM
Note: The following technical information and data should be considered representative
4. Handling strength determined per 3M test method C-3179. Time to handling strength is the time required to achieve 50 psi OLS
5. The cure time is defined as the time required for the adhesive to achieve a minimum of 80% of its ultimate OLS on aluminum.
6. Weight loss by Thermal Gravimetric Analysis reported as that temperature at which 5% weight loss occurs by TGA in air at 5°C
7. Glass transition temperature (Tg) determined using Perkin Elmer (DSC) Analyzer with a heating rate of 20°C (68°F) per minute.
8. Coefficient of thermal expansion determined using DuPont (TMA) using a heating rate of 10°C (50°F) per minute. Second heat
9. Thermal conductivity determined using ASTM C177 and C-matic Instrument with 2 in. diameter samples.
Product
Physical:
Color
Shore D Hardness
(ASTM D 2240)
Time to Handling Strength
Cure Time
Thermal:
Wt. loss by Thermal
Gravimetric Analysis
Glass Transition Temp
Coefficient of Thermal
Expansion (in./in./°C)
Thermal Conductivity
(btu-ft./sq. ft.-hr. °F)
Electrical:
Dielectric Strength
(ASTM D 149)
Volume Resistivity
(ASTM D 257)
strength to aluminum.
(41°F) rise per minute per ASTM 1131-86 Test Procedures.
Second heat values given.
values given.
or typical only and should not be used for specification purposes.
5
6
9
8
7
- 2 -
4
24-48 hours @ 23°C (73°F)
15-20 min. @ 23°C (73°F)
209 x 10
60 x 10
0.107 @ 46°C (115°F)
5% @ 307°C (585°F)
(+140°F to +248°F)
3.5 x 10
(-38°F to +68°F)
DP-100 Clear
Scotch-Weld
860 volts/mil
Translucent
33°C (91°F)
-6
Adhesive
-6
(-40°C to +20°C)
80-85
(60°C to 120°C)
12
ohm-cm
24-48 hours @ 23°C (73°F)
15-20 min. @ 23°C (73°F)
149 x 10
29 x 10
DP-100 NS Translucent
0.106 @ 45°C (113°F)
(+122°F to +230°F)
2.2 x 10
(-56°F to +86°F)
Scotch-Weld
1100 volts/mil
Translucent
34°C (86°F)
-6
Adhesive
-6
(-50°C to +30°C)
80-85
(50°C to 110°C)
14
ohm-cm