DE2E3KH222MA3B Murata, DE2E3KH222MA3B Datasheet - Page 54
![Ceramic Disc Capacitors Class X1 Y2 2200pF 250Vac E 20%](/photos/16/29/162973/113p01_sml.jpg)
DE2E3KH222MA3B
Manufacturer Part Number
DE2E3KH222MA3B
Description
Ceramic Disc Capacitors Class X1 Y2 2200pF 250Vac E 20%
Manufacturer
Murata
Series
DE2r
Specifications of DE2E3KH222MA3B
Voltage Rating
250 Volts
Operating Temperature Range
- 25 C to + 125 C
Termination Style
Radial
Product
Ceramic Disc Capacitors - Other Various
Dimensions
10 mm Dia.
Capacitance
2200 pF
Tolerance
20 %
Temperature Coefficient
E
Lead Spacing
7.5 mm
Capacitor Dielectric Type
CERAMIC DISC AND PLATE
Tolerance,
20%
Tolerance, -
20%
Temp, Op. Max
125(DEGREE C)
Temp, Op. Min
-25(DEGREE C)
Pitch,
ROHS COMPLIANT
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
10
!Note
52
No.
13
14
15
16
17 Life
*
*
DEC Series (Class1, 2 / DC6.3kV) Specifications and Test Methods
DEC Series Specifications and Test Methods
1
2
"Room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
"C" expresses nominal capacitance value (pF).
Continued from the preceding page.
Soldering Effect
(On-Preheat)
Temperature
and Immersion
Cycle
Humidity (Under
Steady State)
Humidity
Loading
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please review our product specifications or consult the approval sheet for product specifications before ordering.
Item
Appearance
Capacitance
Change
Dielectric Strength
(Between Lead
Wires)
Appearance
Capacitance
Change
Q
D.F.
I.R.
Dielectric Strength
(Between Lead
Wires)
Appearance
Capacitance
Change
Q
D.F.
I.R.
Appearance
Capacitance
Change
Q
D.F.
I.R.
Appearance
Capacitance
Change
Q
D.F.
I.R.
No marked defect
Char. SL: Within ±2.5%
Char. B: Within ±5%
Char. E: Within ±15%
Per item 4.
No marked defect
Char. SL: Within ±3%
Char. B: Within ±10%
Char. E: Within ±20%
Char. SL: 275+5/2C*
Char. B, E: 4.0% max.
2000MΩ min.
Per item 4.
No marked defect
Char. SL: Within ±5%
Char. B: Within ±10%
Char. E: Within ±20%
Char. SL: 275+5/2C*
Char. B, E: 5.0% max.
1000MΩ min.
No marked defect
Char. SL: Within ±7.5%
Char. B: Within ±10%
Char. E: Within ±20%
Char. SL:
100+10/3C*
200 min. (30pF min.)
Char. B, E: 5.0% max.
500MΩ min.
No marked defect
Char. SL: Within ±3%
Char. B: Within ±10%
Char. E: Within ±20%
Char. SL: 275+5/2C*
Char. B, E: 4.0% max.
2000MΩ min.
350 min. (30pF min.)
350 min. (30pF min.)
350 min. (30pF min.)
2
min. (30pF under)
Specifications
2
2
2
min. (30pF under)
min. (30pF under)
min. (30pF under)
First the capacitor should be
stored at 120+0/-5°C for
60+0/-5 sec.
Then, as in the figure, the lead
wires should be immersed in
solder of 260+0/-5°C up to 1.5 to
2.0mm from the root of terminal
for 7.5+0/-1 sec.
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
Post-treatment: Capacitor should be stored for 4 to 24 hrs. at
The capacitor should be subjected to 5 temperature cycles,
then consecutively to 2 immersion cycles.
<Temperature Cycle>
<Immersion Cycle>
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 4 to 24 hrs. at
Set the capacitor for 500+24/-0 hrs. at 40±2°C in 90 to 95%
relative humidity.
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
Apply the rated voltage for 500+24/-0 hrs. at 40±2°C in 90 to
95% relative humidity. (Charge/Discharge currentV50mA.)
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
Post-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Apply a DC voltage of 150% of the rated voltage for
1000+48/-0 hrs. at 85±2°C with a relative humidity of 50% max.
(Charge/Discharge currentV50mA.)
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
Post-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Step
1
2
Temperature (°C)
then placed at room condition*
before initial measurements. (Char. B, E)
then placed at room condition*
before initial measurements. (Char. B, E)
then placed at room condition*
before initial measurements. (Char. B, E)
then placed at room condition*
before initial measurements. (Char. B, E)
then placed at room condition*
before initial measurements. (Char. B, E)
Step
room condition.*
room condition.*
room condition.*
room condition.*
room condition.*
then placed at room condition*
(Char. B, E)
room condition.*
then placed at room condition*
(Char. B, E)
65+5/-0
1
2
3
4
0±3
Temperature (°C)
Test Method
Room Temp.
Room Temp.
-25±3
85±3
Time (min)
1
1
1
1
1
1
(Char. SL)
(Char. B, E)
(Char. SL)
(Char. SL)
15
15
Cycle time: 5 cycles
Cycle time: 2 cycles
Thermal
Screen
Immersion Water
Time (min)
Clean water
1
Salt water
1
1
1
1
1
1
for 24±2 hrs.
for 24±2 hrs.
for 24±2 hrs.
for 24±2 hrs.
for 24±2 hrs.
30
30
3
3
for 24±2 hrs.
for 24±2 hrs.
Capacitor
Molten
Solder
1.5
to 2.0mm
C85E.pdf
Jul.13,2011