C1005C0G1H080C TDK Corporation, C1005C0G1H080C Datasheet - Page 54

• Manufacturer Part Number: C1005C0G1H080C
• Description: CAP CER 8.0PF 50V C0G 0402
• Manufacturer: TDK Corporation
• Series: Cr

Specifications of C1005C0G1H080C

• Capacitance: 8.0pF
• Tolerance: ±0.25pF
• Package / Case: 0402 (1005 Metric)
• Voltage - Rated: 50V
• Temperature Coefficient: C0G, NP0
• Mounting Type: Surface Mount, MLCC
• Operating Temperature: -55°C ~ 125°C
• Features: Low ESR
• Applications: General Purpose
• Size / Dimension: 0.039" L x 0.020" W (1.00mm x 0.50mm)
• Thickness: 0.50mm
• Voltage Rating: 50 Volts
• Operating Temperature Range: - 55 C to + 125 C
• Temperature Coefficient / Code: C0G (NP0)
• Product: General Type MLCCs
• Dimensions: 0.5 mm W x 1 mm L x 0.5 mm H
• Termination Style: SMD/SMT
• Dc: 08+
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Ratings: -
• Lead Spacing: -
• Lead Free Status / Rohs Status: Lead free / RoHS Compliant
• Other names: 445-4890-2; C1005COG1H080C

• All specifications are subject to change without notice. Please read the precautions before using the product.
US Catalog // C Series — General Application // Version A11
No.
11
12
General
Specifications
Item
Solderability
Resistance to solder heat
External
appearance
Capacitance
Q (Class 1)
D.F. (Class 2)
Insulation
Resistance
Voltage
Proof
Performance
New solder to cover over 75% of
termination.
25% may have pinholes or rough spots
but not concentrated in one spot.
Ceramic surface of A sections shall not
be exposed due to melting or shifting of
termination material.
No cracks are allowed and terminations
shall be covered at least 60% with new
solder.
Meet the initial spec.
Meet the initial spec.
No insulation breakdown or other
damage.
Characteristics
Class 1
Class 2
Rated Capacitance
C ≥ 30pF
C < 30pF
C0G
X5R
X7R
Y5V
C : Rated capacitance (pF)
Change from the
value before test
Capacitance drift within
±2.5% or ±0.25pF,
whichever larger.
± 7.5 %
± 7.5 %
± 20 %
A section
Q
1,000 min.
400+20×C min.
C Series — General Application
Test or Inspection Method
Completely soak both terminations in
solder at 235±5ºC for 2±0.5s.
Solder: H63A (JIS Z 3282)
Flux: Isopropyl alcohol (JIS K 8839)
Completely soak both terminations in solder at
260±5ºC for 5±1s.
Preheating condition
Flux: Isopropyl alcohol (JIS K 8839)
Solder: H63A (JIS Z 3282)
Leave the capacitor in ambient conditions for 6 to 24h
(Class 1) or 24±2h (Class 2) before measurement.
Temp.: 150±10ºC
Time: 1 to 2min.
Rosin (JIS K 5902) 25% solid solution.
Rosin (JIS K 5902) 25% solid solution.