DEBE33D472ZA2B Murata Electronics North America, DEBE33D472ZA2B Datasheet - Page 50
![CAP CER 4700PF 2KVDC E3 RAD](/photos/10/45/104544/dea_deb_series_pink_fig_2-1617_t073_sml.jpg)
DEBE33D472ZA2B
Manufacturer Part Number
DEBE33D472ZA2B
Description
CAP CER 4700PF 2KVDC E3 RAD
Manufacturer
Murata Electronics North America
Series
DEBr
Specifications of DEBE33D472ZA2B
Capacitance
4700pF
Voltage - Rated
2000V (2kV)
Tolerance
-20%, +80%
Temperature Coefficient
E
Mounting Type
Through Hole
Operating Temperature
-25°C ~ 85°C
Features
High Voltage
Applications
General Purpose
Package / Case
Radial - Disc
Size / Dimension
0.433" Dia (11mm)
Thickness
5.00mm Max
Lead Spacing
0.197" (5.00mm)
Lead Style
Straight
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Ratings
-
Other names
490-4246
9
!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
48
No.
13
14
15
16
17 Life
* "room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
DEB Series Specifications and Test Methods
Continued from the preceding page.
Soldering Effect
(On-Preheat)
Temperature
and Immersion
Cycle
Humidity (Under
Steady State)
Humidity
Loading
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
Item
Appearance
Capacitance
Change
Dielectric Strength
(Between Lead
Wires)
Appearance
Capacitance
Change
D.F.
I.R.
Dielectric Strength
(Between Lead
Wires)
Appearance
Capacitance
Change
D.F.
I.R.
Appearance
Capacitance
Change
D.F.
I.R.
Appearance
Capacitance
Change
D.F.
I.R.
No marked defect
Char. B: Within ±5%
Char. E: Within ±15%
Char. F: Within ±20%
Per item 4.
No marked defect
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Char. B, E: 4.0% max.
Char. F: 7.5% max.
2000MΩ min.
Per item 4.
No marked defect
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Char. B, E: 5.0% max.
Char. F: 7.5% max.
1000MΩ min.
No marked defect
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Char. B, E: 5.0% max.
Char. F: 7.5% max.
500MΩ min.
No marked defect
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Char. B, E: 4.0% max.
Char. F: 7.5% max.
2000MΩ min.
Specifications
First the capacitor should be
stored at 120+0/-5°C for
60+0/-5 sec.
Then, as in figure, the lead wires
should be immersed in solder of
260+0/-5°C up to 1.5 to 2.0mm
from the root of terminal for
7.5+0/-1 sec.
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 4 to 24 hrs. at
The capacitor should be subjected to 5 temperature cycles,
then consecutively to 2 immersion cycles.
<Temperature Cycle>
<Immersion Cycle>
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 4 to 24 hrs. at
Set the capacitor for 500+24/-0 hrs. at 40±2°C in 90 to 95%
relative humidity.
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
Apply the rated voltage for 500+24/-0 hrs. at 40±2°C in 90 to
95% relative humidity. (Charge/Discharge currentV50mA)
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Apply a DC voltage of 150% of the rated voltage for
1000+48/-0 hrs. at 85±2°C with a relative humidity of 50% max.
(Charge/Discharge currentV50mA)
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Post-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
Step
1
2
Temperature (°C)
then placed at room condition* for 24±2 hrs.
before initial measurements.
then placed at room condition* for 24±2 hrs.
before initial measurements.
then placed at room condition* for 24±2 hrs.
before initial measurements.
then placed at room condition* for 24±2 hrs.
before initial measurements.
then placed at room condition* for 24±2 hrs.
before initial measurements.
Step
room condition*.
room condition*.
room condition*.
then placed at room condition* for 24±2 hrs.
then placed at room condition* for 24±2 hrs.
65+5/-0
1
2
3
4
0±3
Temperature (°C)
Test Method
Room Temp.
Room Temp.
-25±3
85±3
Time (min)
15
15
Cycle time: 5 cycle
Cycle time : 2 cycle
Thermal
Screen
Immersion Water
Time (min)
Clean water
Salt water
30
30
3
3
Capacitor
Molten
Solder
1.5
to 2.0mm
C85E.pdf
08.10.29