DEA1X3D221JA2B Murata Electronics North America, DEA1X3D221JA2B Datasheet - Page 14
![CAP CER DISC 220PF 2KV SL RAD](/photos/10/46/104696/dehr33a681ka2b_sml.jpg)
DEA1X3D221JA2B
Manufacturer Part Number
DEA1X3D221JA2B
Description
CAP CER DISC 220PF 2KV SL RAD
Manufacturer
Murata Electronics North America
Series
DEAr
Specifications of DEA1X3D221JA2B
Capacitance
220pF
Voltage - Rated
2000V (2kV)
Tolerance
±5%
Temperature Coefficient
SL
Mounting Type
Through Hole
Operating Temperature
20°C ~ 85°C
Features
High Voltage
Applications
General Purpose
Package / Case
Radial - Disc
Size / Dimension
0.394" Dia (10mm)
Thickness
5.00mm Max
Lead Spacing
0.197" (5.00mm)
Lead Style
Straight
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Ratings
-
Other names
490-4176
4
!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
Operating Temperature Range: -25 to +125°C (-25 to +85°C in case of the standard of UL)
12
No.
*
Type KY/KH/KX Specifications and Test Methods
1
2
3
4
5
6
7
8
Specifications and Test Methods
1
Apply to Type KY/KH/KX
"C" expresses nominal capacitance value (pF).
Appearance and Dimensions
Marking
Capacitance
Dissipation Factor (D.F.)
Q
Insulation Resistance (I.R.)
Dielectric
Strength
Temperature Characteristics
Solderability of Leads
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
Item
Between Lead
Wires
Body
Insulation
No marked defect on appearance form and
dimensions are within specified range.
To be easily legible
Within specified tolerance
10000MΩ min.
No failure
No failure
Lead wire should be soldered with uniform coating
on the axial direction over 3/4 of the circumferential
direction.
(Temp. range: -25 to +85°C)
(Temp. range: +20 to +85°C)
Char.
Char.
Char.
B, E
SL
SL
F
B
E
F
Temperature Coefficient
QU400+20C *
QU1000
Capacitance Change
+350 to -1000ppm/°C
Specifications
Specifications
Within ±10%
Within
Within
D.F.V2.5%
D.F.V5.0%
+20
+30
-55
-80
1
(CU30pF)
(CF30pF)
%
%
The capacitor should be visually inspected for evidence of
defect.
Dimensions should be measured with slide calipers.
The capacitor should be visually inspected.
The capacitance, dissipation factor and Q should be measured
at 20˚C with 1±0.1kHz (char. SL: 1±0.1MHz) and AC5V(r.m.s.)
max.
The insulation resistance should be measured with
DC500±50V within 60±5 sec. of charging.
The voltage should be applied to the capacitor through a
resistor of 1MΩ.
The capacitor should not be damaged when test voltages of
Table 1 are applied between the lead wires for 60 sec.
First, the terminals of the capacitor
should be connected together. Then,
as shown in figure at right, a metal
foil should be closely wrapped around
the body of the capacitor to the
distance of about 3 to 4mm from
each terminal.
Then, the capacitor should be inserted
into a container filled with metal balls
of about 1mm diameter. Finally, AC
voltage of Table 2 is applied for 60 sec. between the capacitor
lead wires and metal balls.
The capacitance measurement should be made at each step
specified in Table 3.
The lead wire of a capacitor should be dipped into molten
solder for 2±0.5 sec.
The depth of immersion is up to about 1.5 to 2.0mm from the
root of lead wires.
Temp. of solder: Lead Free Solder (Sn-3Ag-0.5Cu) 245±5°C
Type
Type
Step
KH
KH
KY
KX
KY
KX
1
2
3
4
5
In case of lead spacing F=7.5mm AC2600V(r.m.s.)
In case of lead spacing F=5mm AC2000V(r.m.s.)
<Table 2>
H63 Eutectic Solder 235±5°C
<Table 3>
AC2600V(r.m.s.)
AC2600V(r.m.s.)
AC4000V(r.m.s.)
Temperature (ºC)
Test Voltage
Test Method
-25±2
20±2
20±2
85±2
20±2
<Table 1>
AC2600V(r.m.s.)
AC4000V(r.m.s.)
Continued on the following page.
Test Voltage
Metal
Foil
about
3 to 4mm
Metal
Balls
C85E.pdf
08.10.29