GRM31CF50J226ZE01L Murata Electronics North America, GRM31CF50J226ZE01L Datasheet - Page 2
![CAP CER 22UF 6.3V Y5V 1206](/photos/10/40/104028/1206_murata_mlcc_caps_sml.jpg)
GRM31CF50J226ZE01L
Manufacturer Part Number
GRM31CF50J226ZE01L
Description
CAP CER 22UF 6.3V Y5V 1206
Manufacturer
Murata Electronics North America
Series
GRMr
Datasheets
1.GNM1M2R71E472MA01D.pdf
(4 pages)
2.GRM033R60J104KE19D.pdf
(3 pages)
3.GRM31CF50J226ZE01L.pdf
(1 pages)
Specifications of GRM31CF50J226ZE01L
Capacitance
22µF
Voltage - Rated
6.3V
Tolerance
-20%, +80%
Temperature Coefficient
Y5V (F)
Mounting Type
Surface Mount, MLCC
Operating Temperature
-30°C ~ 85°C
Applications
General Purpose
Package / Case
1206 (3216 Metric)
Size / Dimension
0.126" L x 0.063" W (3.20mm x 1.60mm)
Thickness
1.60mm
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Features
-
Ratings
-
Lead Spacing
-
Other names
490-1846-2
!Note
No.
10
11 Vibration
12 Deflection
13
*2: GRM31CR60J107, GRM31CD80G107: 0.15 max.
*3: GRM31CR71E106: 0.125 max.
GRM Series Specifications and Test Methods (2)
Continued from the preceding page.
Adhesive Strength
of Termination
Solderability of
Termination
1. This Specifications and Test Methods is downloaded from the website of Murata Manufacturing co.,ltd. Therefore, it's specifications are subject to change or our products in it may be discontinued without advance notice.
0.
2. This Specifications and Test Methods has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product
0.
Please check with our sales representatives or product engineers before ordering.
specifications before ordering.
Item
Appearance
Capacitance
D.F.
Appearance
Capacitance
Change
No removal of the terminations or other defects should occur.
No defects or abnormalities
Within the specified tolerance
B1, B3, R1, R6*
C6: 0.125 max.
F1, F5: 0.2 max.
No marking defects
Within 10%
75% of the terminations is to be soldered evenly and
continuously.
2
, R7*
R230
3
Capacitance meter
45
, C7, C8, E7, D7, D8*
Specifications
20
Fig. 1a
Fig.3a
50
Pressurize
45
Pressurizing
speed : 1.0mm/sec.
c
Flexure : V1
Solder resist
Baked electrode or
copper foil
2
: 0.1 max.
Solder the capacitor on the test jig (glass epoxy board) shown
in Fig. 1a using an eutectic solder. Then apply 10N* force in
parallel with the test jig for 10 1sec.
The soldering should be done either with an iron or using the
reflow method and should be conducted with care so that the
soldering is uniform and free of defects such as heat shock.
*1N: GRM02, 2N: GRM03, 5N: GRM15/GRM18
Solder the capacitor on the test jig (glass epoxy board) in the
same manner and under the same conditions as (10).
The capacitor should be subjected to a simple harmonic motion
having a total amplitude of 1.5mm, the frequency being varied
uniformly between the approximate limits of 10 and 55Hz. The
frequency range, from 10 to 55Hz and return to 10Hz, should
be traversed in approximately 1 minute. This motion should be
applied for a period of 2 hours in each of 3 mutually
perpendicular directions (total of 6 hours).
Solder the capacitor on the test jig (glass epoxy board) shown
in Fig. 2a using an eutectic solder. Then apply a force in the
direction shown in Fig. 3a for 5 1 sec. The soldering should be
done by the reflow method and should be conducted with care
so that the soldering is uniform and free of defects such as heat
shock.
Immerse the capacitor in a solution of ethanol (JIS-K-8101) and
rosin (JIS-K-5902) (25% rosin in weight proportion) .
Preheat at 80 to 120 C for 10 to 30 seconds.
After preheating, immerse in an eutectic solder solution for
2 0.5 seconds at 230 5 C or Sn-3.0Ag-0.5Cu solder solution
for 2 0.5 seconds at 245 5 C.
GRM02
GRM03
GRM15
GRM18
GRM21
GRM31
GRM32
GRM43
GRM55
GRM02
GRM03
GRM15
GRM18
GRM21
GRM31
GRM32
GRM43
GRM55
Type
Type
0.2
0.3
0.4
1.0
1.2
2.2
2.2
3.5
4.5
0.2
0.3
0.4
1.0
1.2
2.2
2.2
3.5
4.5
Test Method
a
a
Fig. 2a
100
Continued on the following page.
b
c
a
0.56
0.56
0.9
1.5
3.0
4.0
5.0
5.0
7.0
8.0
0.9
1.5
3.0
4.0
5.0
5.0
7.0
8.0
b
b
ø4.5
(GRM02/03/15: t: 0.8mm)
0.23
1.65
0.23
1.65
0.3
0.5
1.2
2.0
2.9
3.7
5.6
0.3
0.5
1.2
2.0
2.9
3.7
5.6
c
c
(in mm)
t: 1.6mm