C2012X5R0J106M TDK Corporation, C2012X5R0J106M Datasheet - Page 54

• Manufacturer Part Number: C2012X5R0J106M
• Description: CAP CER 10UF 6.3V X5R 20% 0805
• Manufacturer: TDK Corporation
• Series: Cr

Specifications of C2012X5R0J106M

• Capacitance: 10µF
• Package / Case: 0805 (2012 Metric)
• Voltage - Rated: 6.3V
• Tolerance: ±20%
• Temperature Coefficient: X5R
• Mounting Type: Surface Mount, MLCC
• Operating Temperature: -55°C ~ 85°C
• Features: Low ESR
• Applications: General Purpose
• Size / Dimension: 0.079" L x 0.049" W (2.00mm x 1.25mm)
• Thickness: 1.25mm
• Tolerance (+ Or -): 20%
• Voltage: 6.3VDC
• Temp Coeff (dielectric): X5R
• Operating Temp Range: -55C to 85C
• Mounting Style: Surface Mount
• Construction: SMT Chip
• Case Style: Ceramic Chip
• Failure Rate: Not Required
• Wire Form: Not Required
• Product Length (mm): 2mm
• Product Depth (mm): 1.25mm
• Product Height (mm): 1.25mm
• Product Diameter (mm): Not Requiredmm
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Ratings: -
• Lead Spacing: -
• Lead Free Status / RoHS Status: Compliant, Lead free / RoHS Compliant
• Other names: 445-1363-2; C2012X5R0J106M; C2012X5R0J106MT; C2012X5R0J106MT

• All specifications are subject to change without notice. Please read the precautions before using the product.
US Catalog // C Series — General Application // Version A11
No.
11
12
General
Specifications
Item
Solderability
Resistance to solder heat
External
appearance
Capacitance
Q (Class 1)
D.F. (Class 2)
Insulation
Resistance
Voltage
Proof
Performance
New solder to cover over 75% of
termination.
25% may have pinholes or rough spots
but not concentrated in one spot.
Ceramic surface of A sections shall not
be exposed due to melting or shifting of
termination material.
No cracks are allowed and terminations
shall be covered at least 60% with new
solder.
Meet the initial spec.
Meet the initial spec.
No insulation breakdown or other
damage.
Characteristics
Class 1
Class 2
Rated Capacitance
C ≥ 30pF
C < 30pF
C0G
X5R
X7R
Y5V
C : Rated capacitance (pF)
Change from the
value before test
Capacitance drift within
±2.5% or ±0.25pF,
whichever larger.
± 7.5 %
± 7.5 %
± 20 %
A section
Q
1,000 min.
400+20×C min.
C Series — General Application
Test or Inspection Method
Completely soak both terminations in
solder at 235±5ºC for 2±0.5s.
Solder: H63A (JIS Z 3282)
Flux: Isopropyl alcohol (JIS K 8839)
Completely soak both terminations in solder at
260±5ºC for 5±1s.
Preheating condition
Flux: Isopropyl alcohol (JIS K 8839)
Solder: H63A (JIS Z 3282)
Leave the capacitor in ambient conditions for 6 to 24h
(Class 1) or 24±2h (Class 2) before measurement.
Temp.: 150±10ºC
Time: 1 to 2min.
Rosin (JIS K 5902) 25% solid solution.
Rosin (JIS K 5902) 25% solid solution.