cl10c101jbnc Samsung Semiconductor, Inc., cl10c101jbnc Datasheet - Page 29

• Manufacturer Part Number: cl10c101jbnc
• Description: Multilayer Ceramic Capacitor
• Manufacturer: Samsung Semiconductor, Inc.

Multilayer Ceramic Capacitor
– Application Method
– Adhesive hardening Characteristics
– Mounting Head Pressure
– Bending Stress
They should be a good insulator.
They should be non-toxic, and not produce harmful gases, nor be harmful when touched.
It is important to use the proper amount of adhesive. Too little and much adhesive will cause
poor adhesion and overflow into the land, respectively.
To prevent oxidation of the terminations, the adhesive must harden at 160 E or less, within
2 minutes or less.
Excessive pressure will cause crack to MLCCs. The pressure of nozzle will be 300g maximum
during mounting.
When double-sided circuit boards are used, MLCCs first are mounted and soldered onto one side
of the board. When the MLCCs are mounted onto the other side, it is important to support the
board as shown in the illustration. If the circuit board is not supported, the crack occur to the
ready-installed MLCCs by the bending stress.
Although the solderability increased by the highly-activated flux, increase of activity in flux may
also degrade the insulation of the chip capacitors. To avoid such degradation, it is recommended
that a mildly activated rosin flux(less than 0.2% chlorine) be used.
Mounting
Flux
nozzle
force
support pin