IRA-E940 Murata Manufacturing, IRA-E940 Datasheet - Page 12

• Manufacturer Part Number: IRA-E940
• Description: (IRA-Exxx) Pyroelectric Infrared Sensors
• Manufacturer: Murata Manufacturing

4
Please read CAUTION and Notice in this catalog for safety. This catalog has only typical specifications. Therefore you are requested
to approve our product specification or to transact the approval sheet for product specification, before your ordering.
! Reliability Test
IRA-E700 series, IRA-E900 series
IRA-E420 series
10
Pyroelectric Infrared Sensor IRA Series Characteristics Data
High Temperature
Low Temperature
Humidity
Heat Cycle
Vibration
Shock
Soldering Heat
Hermetic Sealing
Solderability
High Temperature
Low Temperature
Humidity
Heat Cycle
Vibration
Shock
Soldering Heat
Hermetic Sealing
Solderability
Item
Item
100D for 500 hrs.
Y40D for 500 hrs.
60D, 95% RH for 500 hrs.
20 times of following cycle.
Y25D, 30min.eRoom temp., 30min.h
gRoom temp., 30min.f55D, 30min.
Apply vibration of amplitude of 1.5mm with 10 to 55Hz band to each of 3
perpendicular directions for 60min.
Apply shock of 100G sinewave by standard shock tester to each of 3
perpendicular directions.
Immerse up to 3.0mm from can case in solder bath of 260T5D for 10T1 s.
Conform to MIL-STD-202F chapter 112D, condition D.
Immerse in fluorocarbon bath (FC-40) of 125T5D for 20 s.
Conform to MIL-STD-202F chapter 208B.
Immerse in rosin flax and Immerse up to 2.0 to 2.5mm from can case in
solder bath of 230T5D for 5T0.5 s.
100D for 500 hrs.
Y30D for 500 hrs.
60D, 95% RH for 500 hrs.
20 times of following cycle.
Y25D, 30min.eRoom temp., 30min.h
gRoom temp., 30min.f55D, 30min.
Apply vibration of amplitude of 1.5mm with 10 to 55Hz band to each of 3
perpendicular directions for 60min.
Apply shock of 100G sinewave by standard shock tester to each of 3
perpendicular directions.
Immerse up to 3.0mm from can case in solder bath of 260T5˚C for 10T1 s.
Conform to MIL-STD-202F chapter 112D, condition D.
Immerse in fluorocarbon bath (FC-40) of 125T5D for 20 s.
Conform to MIL-STD-202F chapter 208B.
Immerse in rosin flux and Immerse up to 2.0 to 2.5mm from can case in
solder bath of 230T5D for 5T0.5 s.
Test Conditions
Test Conditions
After test completion, leave for three hours in
normal humidity temperature conditions, and
then measure.
1. External appearance:
2. Sensitivity:
3. Noise:
No generation of bubbles.
More than 95% of the terminal should be covered
by solder.
After test completion, leave for three hours in
normal humidity temperature conditions, and
then measure.
1. External appearance:
2. Sensitivity:
3. Noise:
No generation of bubbles.
More than 95% of the terminal should be covered
by solder.
No significant damage.
Tolerance within 20% deviation from original
value.
Maximum tolerance W100mV of original value
No significant damage.
Tolerance within 20% deviation from original
value.
Maximum tolerance W100mV of original value
Criteria
Criteria
S21E3.pdf 03.2.17