CL21B682KBNC Samsung Electro-Mechanics, CL21B682KBNC Datasheet - Page 22

no-image

CL21B682KBNC

Manufacturer Part Number
CL21B682KBNC
Description
Capacitor, Multilayer Ceramic; 6800pF; Chip; Case 0805; +/-10%; 50VDC; SMD; X7R; 2mm
Manufacturer
Samsung Electro-Mechanics
Datasheet

Specifications of CL21B682KBNC

Brand/series
CL Series
Capacitance
6800 pF
Case Code
0805
Insulation Resistance
10000 Megohms
Length
2.0 mm ± 0.1 mm mm
Material, Element
Ceramic
Package Type
0805
Temperature Coefficient
0 ± 30 ppm⁄°C
Temperature, Operating, Maximum
125 °C
Temperature, Operating, Minimum
-55 °C
Termination
SMT
Thickness
1.25 mm ± 0.1 mm (Max.)
Tolerance
±10 %
Voltage, Rating
50 VDC
Width
1.25 mm ± 0.1 mm mm
NO
14
15
Multilayer Ceramic Capacitor
RESISTANCE
MOISTURE
HUMIDITY
(STEADY
STATE)
ITEM
CAPACITANCE
CAPACITANCE
APPEARANCE
APPEARANCE
RESISTANCE
RESISTANCE
INSULATION
INSULATION
CLASS Ⅰ
CLASS Ⅱ
CLASS Ⅰ
CLASS Ⅱ
Tan δ
Tan δ
Q
Q
NO MECHANICAL DAMAGE SHALL OCCUR
30 ㎊ AND OVER : Q ≥ 350
10 ~30 ㎊
LESS THAN 10pF : Q ≥ 200 + 10 × C
MINIMUM INSULATION RESISTANCE:
1,000 ㏁ OR 50 ㏁·㎌ PRODUCT WHICHEVER IS
SMALLER
NO MECHANICAL DAMAGE SHALL OCCUR
CLASS
30 ㎊ AND OVER : Q ≥ 200
30 ㎊ AND BELOW : Q ≥ 100 + 10/3 × C
MINIMUM INSULATION RESISTANCE:
500 ㏁ OR 25 ㏁·㎌ PRODUCT,
WHICHEVER IS SMALLER.
CHARACTERISTIC
CHARACTERISTIC
CLASS
CHAR.
CHAR.
A,B
A,B
F
F
CLASS Ⅰ
CLASS Ⅰ
OVER
0.075
OVER
AND
MAX
0.075
0.05
25V
AND
MAX
MAX
0.05
25V
A,B
A,B
: Q ≥ 275 + 2.5 × C
F
F
PERFORMANCE
(C 〈 1.0 ㎌ )
(C 〈 1.0 ㎌ )
0.125MAX
(C ≥ 1.0 ㎌ )
0.05 MAX
(C ≥ 1.0 ㎌ )
0.1MAX
0.1MAX
0.05
0.125
MAX
MAX
16V
16V
WITHIN ± 5% OR
± 0.5 ㎊ WHICHEVER
IS LARGER
WITHIN ± 12.5%
WITHIN ± 30%
CAPACITANCE CHANGE
WITHIN ± 7.5% OR
± 0.75 ㎊ WHICHEVER
IS LARGER
WITHIN ± 12.5%
WITHIN ± 30%
WITHIN +30~ - 40%
1005 C>0.47 μ F
1608 C>1.0 μ F
2012 C>4.7 μ F
3216 C>10.0 μ F
3225 C>22.0 μ F
4532 C>47.0 μ F
CAPACITANCE CHANGE
MAX
MAX
MAX
MAX
0.05
0.15
10V
0.05
0.15
10V
0.075
0.195
MAX
MAX
6.3V
0.075
0.195
6.3V
MAX
MAX
MAX
MAX
0.25
MAX
MAX
0.25
0.1
4V
0.1
4V
TEMPERATURE
RELATIVE HUMIDITY:90~95 %RH
TEST TIME
MEASURE AT ROOM TEMPERATURE
AFTER COOLING FOR
CLASS Ⅰ : 24 ± 2 Hr.
CLASS Ⅱ : 48 ± 4 Hr.
APPLIED VOLTAGE :
TEMPERATURE : 40±2 ℃
RELATIVE HUMIDITY:90~95%RH
TEST TIME : 500 +12/-0 Hr.
CURRENT APPLIED : 50㎃ MAX.
<INITIAL MEASUREMENT>
CLASS Ⅱ SHOULD BE MEASURED
INITIAL VALUE AFTER BE HEAT-TREATED
FOR 1 HR IN 150℃+0/-10℃ AND BE LEFT
FOR 48±4HR AT ROOM TEMPERATURE.
<LATTER MEASUREMENT>
CLASSⅠ SHOULD BE MEASURED AFTER
LEFT FOR 24±2 HRS IN ROOM
TEMPERATURE AND HUMIDITY.
CLASS Ⅱ SHOULD BE MEASURED
LATTER VALUE AFTER BE
HEAT-TREATED FOR 1 HR IN 150℃+0/-10
℃ AND BE LEFT FOR 48±4HR AT ROOM
TEMPERATURE.
CLASS Ⅱ
6.3V
Tan δ
(A,B)
6.3V Tanδ
CLASSⅡ
(A,B)
RATED VOLTAGE
TEST CONDITION
1005 C ≥ 0.22 ㎌
1608 C ≥ 2.2 ㎌
2012 C ≥ 4.7 ㎌
3216 C ≥ 10.0 ㎌
3225 C ≥ 22.0 ㎌
4532 C ≥ 47.0 ㎌
5750 C ≥ 100.0 ㎌
0.125 MAX *Condition
: 500 +12/-0 Hr.
1005 C ≥0.22㎌
1608 C ≥2.2㎌
2012 C ≥4.7㎌
3216 C ≥10.0㎌
3225 C ≥22.0㎌
4532 C ≥47.0㎌
5750 C ≥100.0㎌
0.125 MAX *Condition
: 40 ± 2 ℃
- 24 -