SPK10-0.006-00-104 Bergquist, SPK10-0.006-00-104 Datasheet - Page 14
![THERMAL PAD TO-247 .006" K10](/photos/5/95/59598/k10-90__104_sml.jpg)
SPK10-0.006-00-104
Manufacturer Part Number
SPK10-0.006-00-104
Description
THERMAL PAD TO-247 .006" K10
Manufacturer
Bergquist
Series
Sil-Pad® K-10r
Specifications of SPK10-0.006-00-104
Usage
TO-218, TO-220, TO-247
Shape
Rectangular
Outline
25.40mm x 19.05mm
Thickness
0.006" (0.152mm)
Backing, Carrier
Kapton®
Color
Beige
Thermal Resistivity
0.41°C/W
Thermal Conductivity
1.3 W/m-K
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Adhesive
-
Other names
BER120
K10-104
K10-104
12
Base Metal Layer Design Considerations
t
t
The adjacent graph depicts the CTE of the base material in relationship
to the heat spreading capability of the metal. Although Aluminum and
Copper are the most popular base layers used in Thermal Clad, other
metals and composites have been used in applications where CTE mis-
match is a factor. The adjacent table represents standard and non-stan-
dard base layers.
Coefficient Of Thermal Expansion
And Heat Spreading
Coefficient Of Thermal Expansion
And Solder Joints
Solder joint fatigue can be minimized by selecting the correct base
layer to match component expansion. The major concern with ther-
mal expansion is the stress the solder joint experiences in power (or
thermal) cycling. Solder joints are not mechanically rigid. Stress
induced by heating and cooling may cause the joint to fatigue as it
relieves stress. Large devices, extreme temperature differential, badly
mismatched materials, or lead-free minimum solder thickness may all
place increased cyclic strain on solder joints.
Solder joint fatigue is typically first associated with ceramic based
components and with device termination. The section on “Assembly
Recommendations” (page 18-19) covers these issues in more detail.
Copper
Aluminum 5052
Aluminum 6061
Coefficient Of Thermal Expansion
And Heat Spreading
Coefficient Of Thermal Expansion
And Solder Joints
METAL / ALLOY
CONDUCTIVITY
THERMAL
[W/mK]
400
150
150
THERMAL EXPANSION
COEFFICIENT OF
[ppm/K]
17
25
25
t
t
t
t
Strength, Rigidity And Weight
Electrical Connections To Base Plate
Surface Finish
Costs
DENSITY
[g/cc]
8.9
2.7
2.7
Extra-Long Circuits
Finished circuits up to 25" (635mm) long
MODULUS OF
RIGIDITY
[GPa]
44.1
25.9
26
YIELD STRENGTH
[MPa]
310
215
230