0103114 Loctite, 0103114 Datasheet
0103114
Manufacturer Part Number
0103114
Description
SCREWLOCK, 10ML
Manufacturer
Loctite
Series
222r
Specifications of 0103114
Adhesive Type
Anaerobic
Adhesive Applications
Thread Locking
Colour
Pink
Svhc
No SVHC (15-Dec-2010)
Breakaway Torque Max
11N-m
Breakaway Torque Min
3N-m
Cure Time Max
2h
Dispensing Method
Bottle
Gap
RoHS Compliant
Volume
10ml
Rohs Compliant
Yes
PRODUCT DESCRIPTION
LOCTITE
threadlocking material, which is thixotropic and develops low
strength for easy disassembly. The product cures when
confined in the absence of air between close fitting metal
surfaces.
TYPICAL APPLICATIONS
Prevents loosening through vibration and leakage of threaded
fasteners.
adjustment of set screws, small diameter or long engagement
length fasteners where easy disassembly is required without
shearing the screw.
PROPERTIES OF UNCURED MATERIAL
TYPICAL CURING PERFORMANCE
Cure speed vs. substrate
The rate of cure will depend on substrate used. The graph below
shows the breakaway strength developed with time on M10
steel nuts and bolts compared to different materials and tested
according to ISO 10964.
Cure speed vs. bond gap
The rate of cure will depend on the bondline gap. Gaps in
threaded fasteners depend on thread type, quality and size. The
following graph shows shear strength developed with time on
steel pins and collars at different controlled gaps and tested
according to ISO 10123.
Chemical Type
Appearance
Specific Gravity @ 25 C
Viscosity @ 25 C, mPa.s (cP)
Flash Point (TCC), C
Brookfield RVF
Spindle 3 @ 2 rpm
DIN 54453, MV
D = 277 s
100
75
50
25
0
®
-1
@ 20 rpm
PLEASE CONTACT LOCTITE CORPORATION QUALITY DEPARTMENT FOR ASSISTANCE AND RECOMMENDATIONS ON SPECIFICATIONS FOR THIS PRODUCT.
Product 222 is a single component anaerobic
after t=180secs
Particularly suitable for applications such as
5min 10min
Cure Time, Hours
30min 1hr
Dimethacrylate ester
Fluorescent Liquid
Opaque Purple,
ROCKY HILL, CT
Value
5,000
1200
1.05
135
>93
THE TECHNICAL DATA CONTAINED HEREIN ARE INTENDED AS REFERENCE ONLY.
3hr
Typical
6hr
FAX: +1 (860)-571-5473
2,500 to 7,500
800 to 1,600
24hr
90 to 180
Range
NOT FOR PRODUCT SPECIFICATIONS.
72hr
Cure speed vs. temperature
The rate of cure will depend on the ambient temperature.
Graph below shows the breakaway strength developed with time
at different temperatures on M10 steel nuts and bolts and
tested according to ISO 10964.
Cure speed vs. activator
Where cure speed is unacceptably long, or large gaps are
present, applying activator to the surface will improve cure
speed. The graph below shows breakaway strength developed
with time using ACTIVATOR N and T on M10 Zinc Dichromate
steel nuts & bolts and tested according to ISO 10964.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of thermal expansion, ASTM D696, K
Coefficient of thermal conductivity, ASTM C177, W.m
1
Specific Heat , kJ.kg
DUBLIN, IRELAND
100
75
25
100
100
50
50
25
75
75
25
50
0
0
0
Worldwide Version, October 1995
5min 10min
5min10min
Technical Data Sheet
5min10min
FAX: +353-(1)-451 - 9959
-1
K
-1
Cure Time, Hours
Cure Time, Hours
Cure Time, Hours
Product 222
30min 1hr
30min 1hr
30min 1hr
3hr
3hr
3hr
6hr
6hr
-1
6hr
-1
K
-
24hr
24hr 72hr
24hr 72hr
80 x10
0.1
0.3
72hr
-6
0103114 Summary of contents
Page 1
... The following graph shows shear strength developed with time on steel pins and collars at different controlled gaps and tested according to ISO 10123. PLEASE CONTACT LOCTITE CORPORATION QUALITY DEPARTMENT FOR ASSISTANCE AND RECOMMENDATIONS ON SPECIFICATIONS FOR THIS PRODUCT. ROCKY HILL, CT 100 75 ...
Page 2
... This product may be covered by one or more United States or foreign patents or patent applications Loctite is a Registered Trademark of Loctite Corporation, Hartford, CT 06106 TDS 222, October 1995 cure speed and strength. This Loctite Corporation specifically To prevent disclaims all Loctite ...