DP190
Manufacturer Part Number
DP190
Description
Scotch-Weld Epoxy Adhesive
Manufacturer
3M
Series
Scotch-Weld 190r
Datasheet
1.DP-190-GRAY.pdf
(7 pages)
Specifications of DP190
Adhesive Type
Epoxy - 2 Part
Adhesive Applications
Bonding - General Purpose
Color
Clear
Dispensing Method
Dual Cartridge
Volume
1.7fl.oz. (US)
3M
Epoxy Adhesives
DP190 Translucent and Gray
Typical Adhesive
Performance
Characteristics
™
Scotch-Weld
Footnotes:
12. Overlap shear (OLS) strengths were measured on 1 in. wide 1/2 in. overlap specimens. These bonds were made
The following product performance data were obtained in the 3M laboratory under
the conditions specified. The following data show typical results obtained with the
3M™ Scotch-Weld™ Adhesives when applied to properly prepared substrates, cured,
and tested according to the specifications indicated. The data were generated using
the 3M™ EPX™ Applicator System equipped with an EPX applicator static mixer,
according to manufacturer’s directions. Thorough hand mixing should afford
comparable results.
Note: The following technical information and data should be considered representative
Overlap Shear Strength (OLS) to
(Bonds cured 24 hrs @ RT + 2 hrs 160°F [71°C])
Rate of Strength Buildup
(OLS on Etched Aluminum)
Etched Aluminum
Sanded Aluminum (60 grit)
Cold Rolled Steel
Wood, Fir
Glass, Borosilicate
Glass,
Polycarbonate
Acrylic
Fiberglass
ABS
PVC
Polypropylene
1 hr @ RT
6 hrs @ RT
24 hrs @ RT
7 days @ RT
1 mo @ RT
3 mos @ RT
™
individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were
measured at 70°F (21°C) except were noted. (Test per ASTM D 1002-72.)
The separation rate of the testing jaws was 0.1 in. per minute for metals, 2 in. per minute for plastics and 20 in. per minute
for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics,
0.125 in.
or typical only and should not be used for specification purposes.
+3M™ Scotch-Weld™ Primer 3901
- 3 -
12
Bonds tested after:
12
3M™ Scotch-Weld™
DP190 Translucent
DP190 Translucent
Epoxy Adhesive
Epoxy Adhesive
Scotch-Weld
1200 psi
1800 psi
1800 psi
1800 psi
1000 psi
850 psi
850 psi
650 psi
260 psi
300 psi
400 psi
350 psi
400 psi
650 psi
200 psi
800 psi
10 psi
90 psi
3M™ Scotch-Weld™
Epoxy Adhesive
Epoxy Adhesive
Scotch-Weld
DP190 Gray
DP190 Gray
2500 psi
1400 psi
1100 psi
1600 psi
1000 psi
2000 psi
2200 psi
2500 psi
1500 psi
300 psi
300 psi
800 psi
500 psi
700 psi
800 psi
50 psi
10 psi
50 psi