DP-100 FR OFF-WHITE 3M, DP-100 FR OFF-WHITE Datasheet

EPOXY 2 PART ADH, CART 1.7FL.OZ

DP-100 FR OFF-WHITE

Manufacturer Part Number
DP-100 FR OFF-WHITE
Description
EPOXY 2 PART ADH, CART 1.7FL.OZ
Manufacturer
3M
Series
Scotch-Weldr
Datasheet
1.DP-100_FR_OFF-WHITE.pdf (6 pages)

Specifications of DP-100 FR OFF-WHITE

Adhesive Type
Epoxy - 2 Part
Color
Off White
Weight
1.7oz
Volume
50ml
Scotch-Weld
Epoxy Adhesive
DP-100 FR
Product Description
Features
Typical Uncured
Physical Properties
Technical Data
3M™ Scotch-Weld™ Epoxy Adhesive DP-100 FR is a two-part flame retardant
(self-extinguishing) version of Scotch-Weld DP-100. It meets the UL94 V-O Burn
Test requirements and has a work life of 4-8 minutes after mixing. It is ideal for
many applications requiring a self-extinguishing structural epoxy adhesive system.
Note: The following technical information and data should be considered representative
1
2
3
4
• Fast Cure
• Cream Color
• Easy Mixing
• Meets UL 94 V-O (File No. E61941)
• Passes 14 CFR 25.853 (60 Sec. Vertical Burn Test)
• Does not contain brominated or antimony-based flame retardants.
As listed in code Federal Regulations, FAA, DOT Regulations 25.853 paragraph a.
Brookfield RVF #7 spindle at 20 rpm.
Approximate time during which a 20 gram quantity of mixed resin at 73°F (23°C) will adequately wet out on a substrate.
Color may vary from nearly white to yellow/amber. Adhesive performance is not affected by color variation.
Viscosity
@ 23°C (73°F)
Base Resin
Color
Net Weight
Lbs./Gallon
Mix Ratio (B:A)
Worklife
@ 23°C (73°F)
or typical only and should not be used for specification purposes.
TM
3
2
Base (B)
Accelerator (A)
Base (B)
Accelerator (A)
By Volume
By Weight
20 g mixed
1
45,000 - 90,000 cps
40,000 - 120,000 cps
December, 2009
4-8 minutes
10.6 - 11.0
10.1 - 10.5
Cream
Epoxy
1 : 1
1 : 0.95
4

DP-100 FR OFF-WHITE Summary of contents

Page 1

... Technical Data Product Description 3M™ Scotch-Weld™ Epoxy Adhesive DP-100 two-part flame retardant (self-extinguishing) version of Scotch-Weld DP-100. It meets the UL94 V-O Burn Test requirements and has a work life of 4-8 minutes after mixing ideal for many applications requiring a self-extinguishing structural epoxy adhesive system. ...

Page 2

... For specific surface preparations on some common substrates, see the section on surface preparation. 3M™ Scotch-Weld™ Epoxy Adhesive DP-100 FR is supplied in a dual syringe plastic duo-pak cartridge as part of the 3M™ EPX™ Applicator System. To use, simply insert the duo-pak cartridge into the EPX Applicator and start the plunger into the cylinders using light pressure on the trigger ...

Page 3

... Scotch-Weld ™ ™ Epoxy Adhesive DP-100 FR Handling/Application Surface Preparation Information (continued) For high strength structural bonds, paint, oxide films, oils, dust, mold release agents and all other surface contaminants must be completely removed. However, the amount of surface preparation necessary depends on the required bond strength and the environmental aging resistance desired by user ...

Page 4

... The following product performance data were obtained in the 3M laboratory under the conditions specified. The following data show typical results obtained with the 3M™ Scotch-Weld™ Epoxy Adhesive DP-100 FR when applied to properly prepared substrates, cured, and tested according to the specifications indicated. This data was generated using the 3M™ ...

Page 5

... Scotch-Weld ™ Epoxy Adhesive DP-100 FR Typical Adhesive Note: The following technical information and data should be considered representative Performance Characteristics 90° T-Peel (continued) Aluminum, etched 2024 T-3 (.032") 10 T-peel (ASTM D 1876-61T) T-Peel strengths were measured on 1" wide bonds at 73°F (23°C). The testing jaw separation rate was 10 inches per minute. The substrates were 0.032" ...

Page 6

... Scotch-Weld ™ ™ Epoxy Adhesive DP-100 FR Technical Information The technical information, recommendations and other statements contained in this document are based upon tests or experience that 3M believes are reliable, but the accuracy or completeness of such information is not guaranteed. Product Use Many factors beyond 3M’s control and uniquely within user’s knowledge and control can affect the use and performance product in a particular application ...