68015 Loctite, 68015 Datasheet

ACRYLIC ADHESIVE, BOTTLE, 10ML

68015

Manufacturer Part Number
68015
Description
ACRYLIC ADHESIVE, BOTTLE, 10ML
Manufacturer
Loctite
Series
680r
Datasheet
1.68015.pdf (3 pages)

Specifications of 68015

Adhesive Type
Acrylic
Color
Green
Dispensing Method
Bottle
Volume
10ml
Lead Free Status / RoHS Status
Lead free / RoHS Compliant

Available stocks

Company
Part Number
Manufacturer
Quantity
Price
Company:
BOSTOCK HK LIMITED BOSTOCK HK LIMITED
Part Number:
680152001
Manufacturer:
ST
0
PRODUCT DESCRIPTION
LOCTITE
characteristics:
LOCTITE
fitting parts, particularly where low viscosity is required. The
product cures when confined in the absence of air between
close fitting metal surfaces and prevents loosening and
leakage from shock and vibration.
NSF International
Certified to ANSI/NSF Standard 61 for use in commercial and
residential potable water systems not exceeding 82° C. Note:
This is a regional approval. Please contact your local Technical
Service Center for more information and clarification.
TYPICAL PROPERTIES OF UNCURED MATERIAL
TYPICAL CURING PERFORMANCE
Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The graph
below shows the shear strength developed with time on steel
pins and collars compared to different materials and tested
according to ISO 10123.
Technology
Chemical Type
Appearance (uncured)
Fluorescence
Components
Viscosity
Cure
Secondary Cure
Application
Strength
Specific Gravity @ 25 °C
Flash Point - See MSDS
Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):
Spindle , speed r/min
100
75
50
25
1min 5min 10min 30min 1h
0
®
®
680™ is designed for the bonding of cylindrical
680™
provides
Acrylic
Methacrylate ester
Green liquid
Positive under UV light
One component - requires no mixing
Medium
Anaerobic
Activator
Retaining
High
the
LMS
3h 6h
following
1.1
750 to 1,750
LMS
24h
product
LMS
72h
Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. The following
graph shows shear strength developed with time on steel pins
and collars at different controlled gaps and tested according to
ISO 10123.
Cure Speed vs. Temperature
The rate of cure will depend on the temperature. The graph
below shows the shear strength developed with time at
different temperatures on steel pins and collars and tested
according to ISO 10123.
100
100
75
50
25
75
50
25
0
1min 5min 10min 30min 1h
0
1min 5min 10min 30min 1h
LOCTITE
Technical Data Sheet
3h 6h
3h 6h
®
December-2009
680™
24h
24h
72h
72h

68015 Summary of contents

Page 1

... ISO 10123. 100 1 750 to 1,750 LMS 24h 72h Technical Data Sheet ® LOCTITE 0 1min 5min 10min 30min 1min 5min 10min 30min 680™ December-2009 24h 72h 24h 72h ...

Page 2

... LMS (psi) (≥2,800) Environment Motor oil Unleaded gasoline N/mm² ≥24.1 LMS Brake fluid (psi) (≥3,500) Water/glycol 50/50 Ethanol Acetone Henkel Europe +49.89.320800.1800 ® TDS LOCTITE 680™, December-2009 0 - 120 ° 1000 2000 3000 % of initial strength °C 100 h 500 h 125 100 ...

Page 3

... Apply localized heat to the assembly to approximately 250 °C. Disassemble while hot. For Cleanup 1. Cured product can be removed with a combination of soaking in a Loctite solvent and mechanical abrasion such as a wire brush. Loctite Material Specification LMS LMS dated August-23, 1999. Test reports for each batch are available for the indicated properties ...