26231 Loctite, 26231 Datasheet - Page 2
![ACRYLIC ADHESIVE, BOTTLE, 50ML](/photos/24/33/243362/4332526_sml.jpg)
26231
Manufacturer Part Number
26231
Description
ACRYLIC ADHESIVE, BOTTLE, 50ML
Manufacturer
Loctite
Series
262r
Datasheet
1.26231.pdf
(3 pages)
Specifications of 26231
Adhesive Type
Acrylic
Color
Red
Dispensing Method
Bottle
Volume
50ml
Chemical Solution
Dimethacrylate Ether
For Use With
Fasteners Up To 0.75" (20mm) In Diameter
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Cure Speed vs. Activator
Where cure speed is unacceptably long, or large gaps are
present, applying activator to the surface will improve cure
speed. The graph below shows the breakaway strength
developed with time on M10 zinc dichromate steel nuts and
bolts using Activator 7471™ and 7649™ and tested according
to ISO 10964.
TYPICAL PROPERTIES OF CURED MATERIAL
TYPICAL PERFORMANCE OF CURED MATERIAL
Henkel Americas
+860.571.5100
Adhesive Properties
After 24 hours @ 22 °C
After 1 hour @ 22 °C
Physical Properties:
Breakaway Torque, ISO 10964:
Prevail Torque, ISO 10964:
Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m:
Max. Prevail Torque, ISO 10964, Pre-torqued to 5 N·m:
Compressive Shear Strength, ISO 10123:
Compressive Shear Strength, ISO 10123:
Coefficient of Thermal Expansion,
Coefficient of Thermal Conductivity, ISO 8302,
W/(m·K)
Specific Heat, kJ/(kg·K)
ISO 11359-2, K
M10 steel nuts and bolts
M10 steel nuts and bolts
M10 steel nuts and bolts
M10 steel nuts and bolts
Steel pins and collars
Steel pins and collars
100
75
50
25
1min
0
For the most direct access to local sales and technical support visit: www.henkel.com/industrial
5min 10min 30min 1h
-1
N·m
(lb.in.)
N·m
(lb.in.)
N·m
(lb.in.)
N·m
(lb.in.)
N/mm²
(psi)
N/mm²
(psi)
3h 6h
(≥1,450)
(≥435)
(190)
(280)
(340)
(350)
22
32
38
40
≥10
≥3
LMS
LMS
80×10
0.1
0.3
24h
+49.89.320800.1800
-6
Henkel Europe
72h
TYPICAL ENVIRONMENTAL RESISTANCE
Hot Strength
Tested at temperature
Heat Aging
Aged at temperature indicated and tested @ 22 °C
Chemical/Solvent Resistance
Aged under conditions indicated and tested @ 22 °C.
Environment
Motor oil (MIL-L-46152)
Leaded Petrol
Brake fluid
Water/glycol 50/50
Acetone
Ethanol
Cured for 1 week @ 22 °C
Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m:
M10 zinc phosphate steel nuts and bolts:
100
125
100
75
50
25
75
50
25
0
0
0
0
1000
TDS LOCTITE
125
°C
22
22
87
22
22
50
2000
100 h
100
100
100
85
95
95
% of initial strength
®
3000
500 h
262™, December-2009
100
100
85
85
95
95
100
Henkel Asia Pacific
+86.21.2891.8863
1000 h
4000
100
100
75
85
95
95
5000 h
100
100
75
85
95
95
5000
150