D6X39B22 MULTICORE (SOLDER), D6X39B22 Datasheet - Page 2

• Manufacturer Part Number: D6X39B22
• Description: SOLDER WIRE, X39, 22SWG, 500G
• Manufacturer: MULTICORE (SOLDER)

Specifications of D6X39B22

• External Diameter: 0.71mm
• Material Composition: Sn60Pb40
• Melting Temperature: 188°C
• Weight: 500g
• Wire Size Swg: 22SWG
• Bit Temperature: 308°C
• Flux Type: X39, Rosin Based, Halide Free
• Reel Length: RoHS Compliant
• Outer Diameter: 0.71mm
• Solder Alloy: 60/40 Sn/Pb
• Solder Gauge Swg: 22SWG
• Rohs Compliant: No

Americas
Henkel Corporation
15350 Barranca Parkway
Irvine, CA 92618 U.S.A.
949.789.2500
All trademarks, except where noted are the property of Henkel Corp.
RECOMMENDED OPERATING CONDITIONS
Soldering iron: Good results should be obtained using a
range of tip temperatures. However, the optimum tip
temperature and heat capacity required for a hand soldering
process is a function of both soldering iron design and the
nature of the task and care should be exercised to avoid
unnecessarily high tip temperatures for excessive times. A
high tip temperature will increase any tendency to flux
spitting and it may produce some residue darkening.
The soldering iron tip should be properly tinned and this
may be achieved using Multicore cored wire. Severely
contaminated soldering iron tips should first be cleaned and
pre-tinned using Multicore Tip Tinner Cleaner, then wiped
on a clean, damp sponge before re-tinning with Multicore
cored wire.
Soldering process: Multicore cored wires contain a
careful balance of resins and activators to provide clear
residues, maximum activity and high residue reliability,
without cleaning in most situations. To achieve the best
results from Multicore solder wires, recommended working
practices for hand soldering should be observed as follows:
The total process will be very rapid, depending upon
thermal mass, tip temperature and configuration and the
solderability of the surfaces to be joined.
Multicore flux cored solder wires provide fast soldering on
copper and brass surfaces as well as solder coated
materials. The good thermal stability of Multicore fluxes
means they are also well suited to soldering applications
requiring high melting temperature alloys.
Cleaning: Multicore X39 flux cored wires have been
formulated to leave minimal quantities of flux residue and
to resist spitting and fuming.
Cleaning will not be required in most situations but if
necessary this is best achieved using Multicore MCF800
Cleaner (see separate technical data sheet). Other
proprietary solvent or semi-aqueous processes may be
suitable. Saponification may be viable but customers must
ensure that the desired level of cleanliness can be achieved
by their chosen system.
Apply the soldering iron tip to the work surface,
ensuring that it simultaneously contacts the base
material and the component termination to heat both
surfaces adequately. This process should only take a
fraction of a second.
Apply Multicore flux cored solder wire to a part of the
joint surface away from the soldering iron and allow to
flow sufficiently to form a sound joint fillet – this
should be virtually instantaneous. Do not apply
excessive solder or heat to the joint as this may result
in dull, gritty fillets and excessive or darkened flux
residues.
Remove solder wire from the work piece and then
remove the iron tip.
Europe
Henkel Loctite Adhesives Ltd
Technologies House, Wood Lane End
Hemel Hempstead
Hertfordshire HP2 4RQ, United Kingdom
[phone]
GENERAL INFORMATION
For safe handling information on this product, consult
the Material Safety Data Sheet, (MSDS).
Note
The data contained herein are furnished for information only and
are believed to be reliable. We cannot assume responsibility for
the results obtained by others over whose methods we have no
control. It is the user's responsibility to determine suitability for
the user's purpose of any production methods mentioned herein
and to adopt such precautions as may be advisable for the
protection of property and of persons against any hazards that
may be involved in the handling and use thereof. In light of the
foregoing, Henkel Corporation specifically disclaims all
warranties expressed or implied, including warranties of
merchantability or fitness for a particular purpose, arising
from sale or use of Henkel Corporation’s products. Henkel
Corporation
consequential or incidental damages of any kind, including
lost profits.
compositions is not to be interpreted as representation that they
are free from domination of patents owned by others or as a
license under any Henkel Corporation patents that may cover such
processes or compositions. We recommend that each prospective
user test his proposed application before repetitive use, using this
data as a guide. This product may be covered by one or more
United States or foreign patents or patent applications.
X3
The discussion herein of various processes or
specifically