C2012X7R1A106K TDK Corporation, C2012X7R1A106K Datasheet - Page 8

• Manufacturer Part Number: C2012X7R1A106K
• Description: CAP CER 10UF 10V X7R 10% 0805
• Manufacturer: TDK Corporation
• Series: Cr

Specifications of C2012X7R1A106K

• Voltage - Rated: 10V
• Capacitance: 10µF
• Tolerance: ±10%
• Temperature Coefficient: X7R
• Mounting Type: Surface Mount, MLCC
• Operating Temperature: -55°C ~ 125°C
• Features: Low ESR
• Applications: General Purpose
• Package / Case: 0805 (2012 Metric)
• Size / Dimension: 0.079" L x 0.049" W (2.00mm x 1.25mm)
• Thickness: 0.057" (1.45mm)
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Ratings: -
• Lead Spacing: -
• Other names: 445-6857-2

(continued)
No.
10
11
Solderability
Resistance
to solder
heat
Item
Capacitance
Q
(Class1)
External
appearance
D.F.
(Class2)
Insulation
Resistance
Voltage
proof
New solder to cover over 75% of
termination.
25% may have pin holes or rough
spots but not concentrated in one
spot.
Ceramic surface of A sections
shall not be exposed due to
melting or shifting of termination
material.
No cracks are allowed and
terminations shall be covered at
least 60% with new solder.
Meet the initial spec.
Meet the initial spec.
No insulation breakdown or
other damage.
C : Rated capacitance (pF)
Characteristics
Class1
Class2
Capacitance
30pF and over
Under 30pF
Performance
C0G
X5R
X7R
Y5V
—— 7 ——
Change from the
value before test
Capacitance drift
within ± 2.5% or
± 0.25pF,
whichever larger.
400+20×C min.
A section
1,000 min.
± 7.5 %
± 7.5 %
± 20 %
Q
Completely soak both terminations in
solder at 235±5°C for 2±0.5s.
Solder : H63A (JIS Z 3282)
Flux : Isopropyl alcohol (JIS K 8839)
Completely soak both terminations in
solder at 260±5°C for 5±1s.
Preheating condition
Flux : Isopropyl alcohol (JIS K 8839)
Solder : H63A (JIS Z 3282)
Leave the capacitors in ambient
condition for 6 to 24h (Class1) or 24±2h
(Class2) before measurement.
Rosin(JIS K 5902) 25% solid
solution.
Rosin (JIS K 5902) 25% solid
solution.
Temp. : 150±10°C
Time : 1 to 2min.
Test or inspection method