C1812C106M3R2CT500 Kemet, C1812C106M3R2CT500 Datasheet - Page 12

• Manufacturer Part Number: C1812C106M3R2CT500
• Description: Multilayer Ceramic Capacitors (MLCC) - SMD/SMT 25volts 10uF 20% double chip stack
• Manufacturer: Kemet

Specifications of C1812C106M3R2CT500

• Voltage Rating: 25 Volts
• Operating Temperature Range: - 55 C to + 125 C
• Temperature Coefficient / Code: X7R
• Product: Low ESR MLCCs
• Dimensions: 3.2 mm W x 4.5 mm L x 5 mm H
• Termination Style: SMD/SMT
• Capacitance: 10 uF
• Tolerance: 20 %
• Package / Case: 1812 (4532 metric)
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant

Surface Mount Multilayer Ceramic Chip Capacitors –KPS Series – Commercial Grade (X7R Dielectric)
Packaging Information Performance Notes
1. Cover Tape Break Force: 1.0 Kg Minimum.
2. Cover Tape Peel Strength: The total peel strength of the cover tape from the carrier tape shall be:
3. Labeling: Bar code labeling (standard or custom) shall be on the side of the reel opposite the sprocket holes. Refer to EIA-556 and EIA-624.
Figure 3 – Maximum component rotation
Figure 4 – Maximum lateral movement
Figure 5 – Bending radius
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 [phone] • www.kemet.com
The direction of the pull shall be opposite the direction of the carrier tape travel. The pull angle of the carrier tape shall be 165° to 180° from the plane of the
carrier tape. During peeling, the carrier and/or cover tape shall be pulled at a velocity of 300±10 mm/minute.
8mm & 12mm Tape
Bo
12mm & 16mm
Tape Width
Embossed
Carrier
8mm
Ao
R
T
°
0.5 mm maximum
0.5 mm maximum
Bending
Radius
Maximum Component Rotation
8,12
Tape
Width (mm)
16-200
Typical Component Centerline
Typical Pocket Centerline
Punched
Carrier
0.1 Newton to 1.0 Newton (10g to 100g)
0.1 Newton to 1.3 Newton (10g to 130g)
Top View
R
16mm Tape
Peel Strength
Maximum
Rotation (
20
10
1.0 mm maximum
1.0 mm maximum
T
°
)
s
°
Maximum Component Rotation
8,12
72-200
Tape
Width (mm)
16-56
Side View
Maximum
Rotation (
10
20
5
S
°
C1020-4 • 6/22/2010
)
12 12