4008-1"X36YD 3M, 4008-1"X36YD Datasheet - Page 3

• Manufacturer Part Number: 4008-1"X36YD
• Description: TAPE DOUBLE SIDED FOAM 1/8 X 1"
• Manufacturer: 3M
• Series: 4008r

Specifications of 4008-1"X36YD

• Tape Type: Double Coated, Double Sided
• Adhesive: Acrylic, 100
• Backing, Carrier: Polyurethane Foam
• Thickness: 0.125" (125 mils, 3.175mm) 1/8"
• Width: 1.00" (25.40mm)
• Length: 108' (32.9m) 36 yds
• Color: Natural
• Usage: Holding, Joining, Mounting
• Temperature Range: 70 ~ 100°F (21 ~ 38°C)
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Thickness - Adhesive: -
• Thickness - Backing, Carrier, Liner: -
• Other names: 021200-06452; 2120006452; 21200064524; 3M4008; 4008; 4008 1"; 4008 (1/8X1"); 4008 1"; 70-0060-7610-6; 70006076106

*3M™ Adhesive 100 is a firm acrylic pressure sensitive adhesive system. It features high ultimate bond strength, very good high temperature
3M
4004 • 4008 • 4016 • 4026 • 4032 • 4052 • 4056 • 4085
Typical Physical Properties
and solvent resistance and very high shear holding power. Bond strength increases substantially with natural aging.
3M™ Adhesive 740 is a medium-firm rubber-resin pressure sensitive adhesive system. It features good holding power and adhesion to a
wide variety of surfaces including many low surface energy plastics such as polyethylene and polypropylene.
Adhesive Type:*
Adhesive Carrier:
Thickness: Nominal
Thickness: Tolerance:
Color:
Release Liner:
Liner Color:
Approximate Density:
(Foam Only)
Standard Length:
Maximum Length:
Available Width:
Normal Slitting Tolerance:
Normal Tensile:
(“T” Block)
1 in
Jaw Speed 2 in/min
(50 mm/min)
Static Shear:
Tensile Strength:
Elongation:
Temperature Resistance:
Solvent Resistance:
UV Resistance:
Cold Flex at -20°F (-30°C):
Thermal Conductivity:
Dielectric Strength:
Short Term (Minutes, Hours)
Long Term (Days, Weeks)
2
(6.45 cm
™
Measured at various
temperatures and
gram loadings.
(1/2 sq. in. overlap).
Will hold listed
weight for 100 hours.
Double Coated Urethane Foam Tapes
2
)
120°F (49°C)
150°F (66°C)
200°F (93°C)
72°F (22°C)
(watt/metre Kelvin)
(volts/0.025 mm)
BTU/hr/°F/ft
yard (meter)
yard (meter)
inch (mm)
inch (mm)
inch (mm)
inch (mm)
Note: The following technical information and data should be considered representative
psi (kPa)
psi (kPa)
volts/mil
(kg/m
°F (°C)
°F (°C)
Units
(mm)
inch
lb/ft
gms
%
3
or typical only and should not be used for specification purposes.
3
)
2
/ft
Polyurethane Foam Polyurethane Foam Polyurethane Foam Polyurethane Foam
± 1/32 (± 0.8)
0.003 (0.08)
0.025-0.040
Green Plaid
0.031 (0.8)
(0.64-1.02)
240 (1655)
46 (1168)
175 (160)
380 (193)
220 (104)
(200-300)
72 (65.8)
60 (414)
200-300
Natural
(0.062)
0.036
4032
(320)
2000
1500
1000
1050
No apparent degradation when exposed to 7 days in U.V. chamber.
100
20
90
- 3 -
No cracking when flexed around a 1/4 in. (6.4 mm mandrel).
No apparent degradation when exposed to splash
3M™ Double Coated Urethane Foam Tape
tests of most hydrocarbon solvents.
± 1/32 (± 0.8)
0.003 (0.08)
0.025-0.040
Green Plaid
0.031 (0.8)
(0.64-1.02)
225 (1550)
46 (1168)
175 (160)
380 (193)
220 (104)
(200-300)
72 (65.8)
75 (515)
200-300
(0.062)
Black
0.036
4052
(225)
1500
100
110
14
750
750
750
± 1/32 (± 0.8)
(1.142-2.03)
0.0625 (1.6)
0.045-0.080
0.003 (0.08)
Green Plaid
46 (1168)
(200-300)
140 (965)
380 (193)
220 (104)
36 (32.9)
100 (91)
50 (345)
200-300
(0.062)
Black
0.036
(175)
4056
1500
1000
100
100
11
750
750
± 1/32 (± 0.8)
0.003 (0.08)
0.039-0.054
0.045 (1.2)
(1.00-1.45)
46 (1168)
140 (965)
125 (152)
(200-300)
72 (65.8)
100 (91)
45 (310)
200 (93)
200-300
Natural
(0.062)
0.036
4085
(352)
1000
740
100
Tan
22
250
—
—