5952 3/4"X15YD 3M, 5952 3/4"X15YD Datasheet - Page 7
5952 3/4"X15YD
Manufacturer Part Number
5952 3/4"X15YD
Description
TAPE DBL COATED H-DUTY 3/4"X15YD
Manufacturer
3M
Series
VHB™r
Specifications of 5952 3/4"X15YD
Tape Type
Double Coated, Double Sided
Adhesive
Acrylic
Backing, Carrier
Polyethylene Film
Thickness
0.045" (45 mils, 1.143mm)
Thickness - Adhesive
0.040" (40 mils, 1.016mm)
Thickness - Backing, Carrier, Liner
0.0050" (5.0 mils, 0.127mm)
Width
0.75" (19.05mm) 3/4"
Length
45' (13.7m) 15 yds
Color
Black
Usage
General Purpose
Temperature Range
250°F (121°C)
For Use With
A99648 - MODULE BOX ASSY SOLARLOK W/CABLEA99647 - MODULE BOX ASSY SOLARLOK W/CABLEA99646 - MODULE BOX ASSY SOLARLOKA98821 - MODULE BOX ASSEMBLY SOLARLOK
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Other names
00-051115-25522-9
3M5647
70006429198
3M5647
70006429198
3M
Additional Typical Performance Characteristics
Note: The following technical information and data should be considered representative or typical only and should not
Outgassing:
3M™ VHB™
Tapes
4930
4932
4945
TML - Total Mass Loss
VCM - Volatile Condensible Materials
WVR - Water Vapor Regained
NASA Reference Publication, “Outgassing Data
for Selecting Spacecraft Materials”, (11/18/2004)
Available online at http://outgassing.nasa.gov
Resistivity
(ASTM D257)
3M™ VHB™
Tapes
4941
5952
4950
4920
4910
4611
Water Vapor Transmission Rate (WVTR)
(ASTM F1249) at 38°C/100% RH
3M™ VHB™ Tapes
4950
4941
5952
Typical 3M™ VHB™ Tape Properties for Modeling
Thermal Coefficient
of Expansion
Shear Modulus (@25°C, 1 Hz)
(Shear Modulus is both temperature and frequency
dependent).
Youngs Modulus: For VHB tapes the Youngs
Modulus will be about 3 times the Shear Modulus.
Poisson’s Ratio
Dielectric Constant
(ASTM D150)
3M™ VHB™
Tapes
4941 at 1 kHz
5952 at 1 kHz
4950 at 1 kHz
4910 at 1 kHz
4611 at 1 kHz
Burn Characteristics 3M™ VHB™ Tape 5958FR
Meets FAR 25.853 (a) 12 second vertical burn,
Appendix F, Part I (a)(ii).
Meets NBS Smoking Density (ASTM F814/E662).
Meets Toxicity (Draeger Tube ABD0031, AITM
3.0005)
1 x 10
1.8 x 10
4950 Family: 6 x 10
4941 Family: 3 x 10
0.49
at 1 MHz
at 1 MHz
at 1 MHz
at 1 MHz
at 1 MHz
™
be used for specification purposes.
-4
in/in/°F
-4
VHB
mm/mm/°C
% TML
0.77
2.41
1.24
Dielectric
Constant
5
5
™
2.29
1.99
2.14
1.95
2.28
1.99
3.21
2.68
2.80
2.43
14.0 g/(m
25.6 g/(m
37.1 g/(m
Pa
Pa
Tapes
%VCM
0.01
0.66
0.01
2
2
2
Volume Resistivity
day)
day)
day)
Dissipation
(in ohm-cm)
Factor
0.0245
0.0374
0.0065
0.0506
0.0227
0.0370
0.0214
0.0595
0.0130
0.0564
2.1 x 10
2.5 x 10
1.5 x 10
1.7 x 10
3.1 x 10
1.4 x 10
%WVR
0.21
0.23
0.19
14
14
15
15
15
15
Dielectric Breakdown Strength
(ASTM D149)
3M™ VHB™
Tapes
4941
4926
5952
5925
4950
4920
4910
4611
Thermal Conductivity - K-value
3M™ VHB™
Tapes
4941
5952
4950/4945
4910
4611
R-Value = thickness
(When units of K-value are
BTU-in/hr ft
is given in inches.)
Test Method
• Tape between stainless steel and aluminum foil.
• 72 hours dwell at room temperature.
• Solvent immersion for 72 hours.
• Test within 45 minutes after removing from solvent.
• 90° peel angle.
• 12 in./min. rate of peel.
• Peel adhesion compared to control.
%
Note: Continuous submersion in chemical solutions is not recommended. The above information is presented to show that
A
d
h
e
e
s
v
i
K-value
R
e
e
n
o
n
t
t
i
100
occasional chemical contact should not be detrimental to tape performance in most applications in ordinary use.
Surface Resistance
BTU in/
hr ft
Solvent and Fuel Resistance
90
80
70
60
50
40
30
20
10
(in ohms/square)
0
0.53
0.37
0.63
1.09
0.77
2
°F and thickness
2
2.7 x 10
°F
(in volts/mil)
>10
>10
>10
>10
>10
10W30 Motor Oil
Glycol Antifreeze
Hydraulic Fluid
16
16
16
16
16
360
330
455
520
460
640
630
330
Salt Water
(w/mK)
Water
(0.08)
(0.05)
(0.09)
(0.16)
(0.11)
14
- 7 -
A current list can be found at www.ul.com (select certifications, search file MH17478)
3M™ VHB™ Tapes/
Product Families
4919F, 4926, 4936,
4936F, 4941, 4941F,
4947F, 4956, 4956F,
4979F
4920, 4930, 4950
4945, 4946
5915, 5915P, 5925,
5925P, 5930, 5930P,
5952, 5952P 5962,
5962P
5915, 5925, 5930, 5952
5962
5952
4991
4611, 4646, 4655
4905, 4910
Category QOQW2 Component - Polymeric Adhesive Systems, Electrical Equipment
Kerosene
UL746C Listings - File MH 17478
Isopropyl Alcohol
Jet Fuel
Substrates
Ceramic
Aluminum, Galvanized steel, stainless
steel, enameled steel, nickel coated
ABS, glass (with or without silane
coating) PVC, glass/epoxy, PBT,
polycarbonate, acrylic/polyurethane
paint, polyester paint
ABS
Aluminum, galvanized steel,
enameled steel, stainless steel,
ceramic, glass/epoxy
PBT, Acrylic
ABS, Polycarbonate, Rigid PVC
Phenolic, aluminum, galvanized
steel, alkyd enamel
ABS, polycarbonate, polyimide,
stainless steel, acrylic/polyurethane
paint, polyester paint
unplasticized PVC
Polycarbonate, Primer 94 coated
polycarbonate, aluminum, acrylic/
polyurethane paint, galvanized steel,
steel, polyester paint, epoxy/polyester
paint, epoxy paint, glass (with or
without silane coating), stainless
steel, enameled steel, glass epoxy,
polybutylene terephthalate, Nylon
Noryl
Rigid PVC, ABS
Acrylic
Acrylic
Cellulose Acetate Butyrate
Polycarbonate, aluminum, acrylic/
polyurethane paint, polyester paint
Stainless steel, aluminum, galvanized
steel, glass, glass/epoxy, phenolic
Nylon, polycarbonate
ABS, rigid PVC
Polycarbonate, aluminum,
acrylic/polyurethane paint
3M™ VHB™ Tapes
®
(PPE) polyphenenlene ether
Gasoline
®
,
Minimum
Temperature Rating
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
-35°C
MEK
Maximum
110°C
110°C
110°C
110°C
90°C
75°C
90°C
75°C
90°C
75°C
90°C
75°C
90°C
80°C
90°C
90°C
90°C
75°C
90°C
100
90
80
70
60
50
40
30
20
10
0