832C-375ML MG Chemicals, 832C-375ML Datasheet - Page 2

• Manufacturer Part Number: 832C-375ML
• Description: POTTING COMPOUND CLR 2PART 375ML
• Manufacturer: MG Chemicals
• Series: 832r
• Type: Potting Compound, 2 Partr

Specifications of 832C-375ML

• Product: Epoxy Compounds
• Size: 12 oz
• Chemical Component: Alkyl Glycidyl Ether/Epichlorohydrin and Biphenyl A
• Density, Vapor: Air
• Flash Point: 190
• Odor: Odorless
• Physical State: Liquid
• Primary Type: Adhesive
• Special Features: Kit
• Specific Gravity: 1.13
• Standards: RoHS Compliant
• Weight: 12 Oz.
• For Use With/related Products: Sealing Electronic Components
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Features: -
• Lead Free Status / Rohs Status: Lead free / RoHS Compliant
• Other names: 473-1083

Disclaimer:
This information is believed to be accurate. It is intended for professional end users having the skills to evaluate and use the data
properly. M.G. Chemicals Ltd. Does not guarantee the accuracy of the data and assumes no liability in connection with damages
incurred while using it.
Shore
Coefficient of Thermal Expansion
Lap shear strength
Curing Time (100g)
Cured Properties - Temperature
Constant Service Temperature
Intermediate Service Temperature
Heat deflection temp. 264 psi
Cured Properties - Electrical
Volume Resistivity (ASTM D257)
Surface Resistivity (ASTM D257)
Dielectric Constant (ASTM D150)
Dielectric strength (0.114"thk)
Insulative
Conductive
Chemical and Solvent Resistance
Hydrocloric Acid
Isopropyl Alcohol
Ethyl Lactate
Acetone
Xylene
Iso hexanes
Mineral spirits
@ room temp.
@ 65°C
@ 80°C
@ 100°C
Hardness
ASTM D 2240
ASTM E 831
ASTM 1002
140°C (284°F)
145°C (293°F)
ASTM D 648
1.22 x 10
5.50 x 10
3.23 @ 60Hz
3.19 @ 10
2.99 @ 10
ASTM D 149
Yes
No
Change after
3 days
< 0%
< 0.3 %
< 3 %
< 7%
< 2%
< 5 %
< 0.3 %
16
15
3
6
ohm · cm
ohm · cm
Hz
Hz
85 (initial) - 85 (10 sec) averages
0.036" / 10 " @ 32°F, 0.020"/10" @72°F
702 psi
24 hours
60 minutes
45 minutes
35 minutes
43.548°C (92.22°F)
425 V / mil, 60 Hz
Change after
45 days
< 1 %
< 1 %
< 7 %
destroyed
< 9 %
< 8 %
< 0.3 %