(5) Soldering Conditions
· The LEDs can be soldered in place using the reflow soldering method.
· Recommended soldering conditions
2.5 ~ 5°C / sec.
· Occasionally there is a brightness decrease caused by the influence of heat or ambient atmosphere
· The encapsulated material of the LEDs is silicone. Therefore the LEDs have a soft surface on the
· Repairing should not be done after the LEDs have been soldered.
· Reflow soldering should not be done more than two times.
· When soldering, do not put stress on the LEDs during heating.
· After soldering, do not warp the circuit board.
guarantee on the LEDs after they have been assembled using the dip soldering method.
during air reflow.
top of package.
Precautions should be taken to avoid the strong pressure on the encapsulated part.
the chip mounter, the picking up nozzle that does not affect the silicone resin should be used.
a double-head soldering iron should be used.
characteristics of the LEDs will or will not be damaged by repairing.
[Recommended soldering pad design]
[Temperature-profile (Surface of circuit board)]
Pre-heat
Pre-heat time
Peak
Soldering time
Condition
temperature
<
Although the recommended soldering conditions are specified in the above table, reflow or hand
soldering at the lowest possible temperature is desirable for the LEDs.
A rapid-rate process is not recommended for cooling the LEDs down from the peak temperature.
1
: Lead Solder>
2.5 ~ 5°C / sec.
120 ~ 150°C
120sec.Max.
Pre-heating
4
120 ~ 150°C
120 sec. Max.
240°C Max.
10 sec. Max.
refer to
Temperature - profile
1.5
The pressure to the top surface will be influence to the reliability of the LEDs.
: Solder resist
It is recommended that the User use the nitrogen reflow method.
9.5
Lead Solder
60sec.Max.
Above 200
1.5
Reflow Soldering
4
°C
240°C Max.
10sec. Max.
1
.
180 ~ 200°C
120 sec. Max.
260°C Max.
10 sec. Max.
refer to
(N
Temperature - profile
2
Use the following conditions shown in the figure.
reflow is recommended.)
Lead-free Solder
It should be confirmed beforehand whether the
(Unit : mm)
-6-
Use the conditions shown to the under figure.
1 ~ 5°C / sec.
<
2
: Lead-free Solder>
2
.
Temperature
Soldering time
1 ~ 5°C / sec.
When repairing is unavoidable,
180 ~ 200°C
120sec.Max.
Pre-heating
Nichia cannot make a
Hand Soldering
60sec.Max.
Above 220°C
350°C Max.
3 sec. Max.
(one time only)
So when using
Nichia STS-DA1-0226
<Cat.No.080519>
260°C Max.
10sec. Max.