832B-375ML MG Chemicals, 832B-375ML Datasheet - Page 2
![POTTING COMPOUND BLK 2PART 375ML](/photos/15/53/155363/832b-375ml_sml.jpg)
832B-375ML
Manufacturer Part Number
832B-375ML
Description
POTTING COMPOUND BLK 2PART 375ML
Manufacturer
MG Chemicals
Series
832r
Type
Potting Compound, 2 Partr
Specifications of 832B-375ML
Product
Epoxy Compounds
Size
12 oz
Chemical Component
Alkyl Glycidyl Ether/Epichlorohydrin and Bisphenol A
Density, Vapor
Air
Flash Point
190
Odor
Odorless
Physical State
Liquid
Primary Type
Adhesive
Special Features
Kit
Specific Gravity
1.13
Standards
RoHS Compliant
Weight
12 Oz.
For Use With/related Products
Sealing Electronic Components
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Features
-
Lead Free Status / Rohs Status
Lead free / RoHS Compliant
Other names
473-1082
Tensile strength (ASTM D 638)
Elongation
Compression strength (ASTM D 695)
Flexural strength (ASTM D 790)
Izod impact strength (ASTM D 256)
Lap Shear Strength (ASTM D 732)
Working time (100g)
Curing Time (100g)
Cured Properties - Temperature
Coefficient of Thermal Expansion
(ASTM E 831)
Constant Service Temperature
Intermediate Service Temperature
Heat Deflection Temp. (264 psi)
(ASTM D 648)
Cured Properties - Electrical
Surface Resistivity (ASTM D 257)
Corrected Dissipation Factor, D
(ASTM D150-98)
Dielectric Constant (ASTM D150-98)
Insulative
Conductive
Breakdown Voltage (ASTM D149-97a)
Dielectric Strength (ASTM D149-97a)
Chemical and Solvent Resistance
Hydrocloric Acid
Isopropyl Alcohol
Ethyl Lactate
Acetone
Xylene
Iso hexanes
Mineral spirits
Modulus
Modulus
@ room temp.
@ 65°C
@ 80°C
@ 100°C
8475 psi
3.3%
14,675 psi
375,000 psi
16,500 psi
427,000 psi
0.443 ft-lbs / inch notch
0.259" thick
957 psi
60 min.
24 hours
60 minutes
45 minutes
35 minutes
0.036" / 10" @ 32°F,
0.013" / 10" @ 72°F
140°C (284°F)
145°C (293°F)
46.638°C (115.95°F)
5.3 x 10
0.008 @ 1KHz
0.013 @ 10KHz
0.018 @ 100KHz
0.017 @ 1MKHz
2.95 @ 1KHz
2.89 @ 10KHz
2.83 @ 100KHz
2.77 @ 1MKHz
Yes
No
51.9 kV
471 V/mil
Change after
3 days
< 0%
< 0.3 %
< 3 %
< 7%
< 2%
< 5 %
< 0.3 %
12
ohm · cm
Change after
45 days
< 1 %
< 1 %
< 7 %
destroyed
< 9 %
< 8 %
< 0.3 %